Influência do pré-alargamento coronário na resistência à fadiga cíclica de instrumentos reciprocantes tratados termicamente / Influence of coronal pre-enlargement on cyclic fatigue resistance of heat-treated reciprocating instruments

Objetivo: O objetivo do presente estudo foi avaliar a influência do pré-alargamento coronário na resistência à fadiga cíclica de dois instrumentos reciprocantes tratados termicamente. Métodos: 20 instrumentos Reciproc Blue (R25 Blue) e 20 instrumentos X1 Blue (X1) foram utilizados para instrumentar blocos de resina simulando um molar superior com três canais radiculares. Os dentes foram divididos em quatro grupos (n=10), de acordo com o instrumento e com a técnica de instrumentação utilizada: grupos R25 e X1 - instrumentação com R25 Blue (25/0.08) ou X1 Blue (25/0.06), respectivamente, sem alargamento prévio; e grupos R25 ou X1 + pré-alargamento cervical - pré-alargamento com os instrumentos ProTaper Universal SX e S1 antes da instrumentação com R25 Blue ou X1. Os instrumentos foram testados com relação à fadiga cíclica utilizando-se um canal simulado de aço inoxidável com ângulo de curvatura de 86 graus e raio de curvatura de 6 mm. Os instrumentos foram acionados utilizando-se o movimento "RECIPROC ALL" do motor endodôntico (VDW) e o tempo de instrumentação até a fratura do instrumento foi contabilizado. Os resultados foram analisados pelo teste t de Student (p<0,05). Resultados: Os instrumentos X1 apresentaram maior resistência à fadiga cíclica do que R25 Blue em ambas as condições testadas (p<0,05). Não houve diferença entre os grupos com e sem pré-alargamento coronário para os instrumentos R25 Blue e X1 (p>0,05). Conclusão: O instrumento X1 Blue apresentou maior resistência à fadiga cíclica do que o Reciproc Blue. O pré-alargamento coronário não foi capaz de aumentar a resistência à fratura por fadiga cíclica dos instrumentos testados (AU).

Objective: The aim of this study was to evaluate the influence of cervical pre-flaring on the cyclic fatigue resistance of two heat-treated reciprocating instruments. Methods: 20 Reciproc Blue (R25 Blue) instruments e 20 X1 Blue File (X1) were used to instrument resin blocks simulating an upper molar with 3 root canals. The specimens were divided into four groups (n=10) according the instrument and type of instrumentation used: R25 and X1 groups: root canal preparation with R25 Blue (25/0.08) ou X1 Blue (25/0.06), without cervical pre-flaring; R25 or X1 + cervical pre-flaring- pre-flaring with ProTaper Universal SX e S1 before instrumentation with R25 Blue or X1 blue. After instrumentation the instruments were tested for cyclic fatigue using a simulated stainless steel root canal with 86 degree bending angle and 6 mm bending radius. The instruments were triggered using the "RECIPROC ALL" motion of a reciprocating endodontic motor (VDW) and the instrumentation time until instrument fracture was accounted. Results were analyzed by Students t-test (p<0.05). Results: Statistical analysis showed that the X1 Blue showed higher resistance to cyclic fatigue than the R25 Blue under both conditions tested (p<0.05). There were no differences between the groups with and without coronary pre-flaring for the R25 Blue and X1 Blue (p<0.05). Conclusion: X1 Blue showed higher resistance to cyclic fatigue than the R25 Blue. The cervical pre-flaring did not increased the resistance to cyclic fatigue fracture of the tested instruments (AU)

AVALIAÇÃO DO CONHECIMENTO DOS ESTUDANTES DOS CURSOS DE MEDICINA E ODONTOLOGIA SOBRE CARCINOMA BUCAL / EVALUATION OF KNOWLEDGE OF MEDICAL AND DENTISTRY COURSE STUDENTS ABOUT ORAL CARCINOMA

Purpose: The aim of the present study was to verify the knowledge of health professionals being educated in the Medical and Dentistry courses about oral cancer, specifically Oral Squamous Cell Carcinoma (OSCC), in view of this being the most prevalent type of cancer of the head and neck. Methods: A questionnaire contained objective questions was applied with the aim of evaluating knowledge about some aspects of OSCC. Students in the clinical cycle of the Course in Medicine and Course in Dentistry participated. Both groups were in the 5th and 8th semesters at the Campuses 1 (C1) and 2 (C2). A total of 454 questionnaires were answered and evaluated, distributed as follows: 301 and 153 from the C1 and C2, respectively. Results: The results show that the students from Medicine of the C1 and C2 were observed to be "Regular" (40.67%) and "Insufficient" (44.58%), respectively. For the course in Dentistry of C1 and C2, the prevalent response was "Good" for courses, 52.67% and 46.38%, respectively. Conclusion: The results revealed an inadequate level of knowledge of OSCC. Despite the knowledge is transmitted, changes are necessary to allow the students more time in clinical practice to reptai knowledge.

Objetivo: O objetivo do presente estudo foi verificar o conhecimento dos profissionais de saúde formados nos cursos de Medicina e Odontologia sobre câncer bucal, especificamente o Carcinoma de Células Escamosas Bucais (CCEB), tendo em vista que este é o tipo de câncer de cabeça e pescoço mais prevalente. Metodologia: Um questionário contendo perguntas objetivas foi aplicado com o objetivo de avaliar o conhecimento sobre alguns aspectos do CCEB. Participaram os alunos do ciclo clínico dos cursos de Medicina e Odontologia. Ambos os grupos estavam no 5º e 8º semestres nos campi 1 (C1) e 2 (C2). Foram respondidos e avaliados 454 questionários, distribuídos da seguinte forma: 301 e 153 do C1 e C2, respectivamente. Resultados: Os resultados mostram que os estudantes de Medicina dos C1 e C2 foram observados como "Regular" (40,67%) e "Insuficiente" (44,58%), respectivamente. Para o curso de Odontologia dos C1 e C2, a resposta predominante foi "boa" para os cursos, 52,67% e 46,38%, respectivamente. Conclusão: Os resultados revelaram um nível inadequado de conhecimento da CCEB. Apesar do conhecimento ser transmitido, são necessárias mudanças para permitir que os alunos tenham mais tempo na prática clínica para reter conhecimento.

Influencia de los Diseños de Agujas Endodónticas en la Irrigación de Conductos Radiculares

RESUMEN: La irrigación del sistema de conductos radiculares con soluciones antibacterianas es considerada una parte esencial de la preparación químico-mecánica. Varios factores influyen en la eficacia de la irrigación del conducto radicular, incluyendo tamaño de la preparación apical y ensanchamiento, distancia de penetración de la aguja con respecto al ápice, flujo y volumen de sustancia de irrigante, dimensión de las agujas y la presencia de curvatura del conducto radicular. El tamaño de la preparación apical y la conicidad afectan el recambio del irrigante, el esfuerzo de corte en las paredes del conducto radicular y la presión en el foramen apical. La colocación de la punta de la aguja más cerca del ápice, permite un recambio de la solución más eficiente, resultando una mejor limpieza y desinfección del conducto radicular. La velocidad del irrigante, al lado de la aguja, en las paredes del conducto opuestas y frente a la salida de la aguja es dependiente del diseño de la aguja. El patrón de flujo y recambio del irrigante de las agujas con extremo abierto es diferente al de las agujas cerradas y las que logran mejor recambio de irrigante en la parte apical del conducto radicular también conducen a un aumento de la presión media en el foramen apical, lo que indica un mayor riesgo de extrusión del irrigante hacia el tejido periapical. El objetivo de esta revisión a la literatura, es evaluar los diferentes diseños de agujas y su influencia en la irrigación del sistema de conductos radiculares.

ABSTRACT: Root canal irrigation with antibacterial solutions is considered an essential part of the chemical-mechanical preparation. Several factors influence the efficacy of root canal irrigation, including apical preparation size and taper, needle penetration distance from the apex, flow and volume of irrigant substance, dimension of the needles and the presence of curvature of the root canal. The apical preparation size and the taper affect irrigant replacement, shear stress on the root canal walls, and pressure on the apical foramen. Placing the tip of the needle closer to the apex, allows more efficient solution exchange, resulting in better cleaning and disinfection of the root canal. The velocity of the irrigant, next to the needle, on the opposite canal walls and in front of the needle outlet is dependent on the design of the needle. The flow and irrigant replacement pattern of open ended needles is different from needles with closed tip. The needles that achieve better irrigant exchange in the apical part of the root canal also lead to an increase in mean pressure in the apical foramen which indicates a greater risk of extrusion of the irrigant into the periapical tissue. The objective of this literature review is to evaluate the different needle designs and their influence on the root canal system irrigation.

Influência da orientação das ranhuras superficiais na flexão rotativa de fios de níquel-titânio / Influence of surface grooves orientation on the cyclic fatigue resistance of NiTi wire

Objetivo: Testar a hipótese nula de que a orientação das ranhuras superficiais não influencia na vida em fadiga de fios de níquel-titânio (NiTi). Material e Métodos: Segmentos de fio de NiTi (Moreli, Sorocaba/SP, Brasil) medindo 30mm e com diâmetro de 0,40mm foram utilizados. As ranhuras foram criadas em relação à direção longitudinal, em 45 e 90 graus. O fio foi analisado sob microscopia eletrônica de varredura e a rugosidade, quantificada por interferometria. O número de ciclos para a fratura (NCF) foi determinado pelo teste de flexão rotativa. Resultados: A rugosidade entre os grupos de 45 e 90 graus apresentou diferenças estatisticamente significativas (p<0,05). O grupo sem ranhuras apresentou o maior NCF (p<0,05). O grupo com ranhuras em 45 graus apresentou maior NCF, em comparação ao grupo com 90 graus (p<0,05). Conclusões: A direção das ranhuras possui influência na vida em fadiga dos fios de NiTi. O NCF aumenta com a redução do ângulo das ranhuras em relação ao longo eixo do fio, independentemente da profundidade das ranhuras (AU).

Objective: this study tested the null hypothesis that the surface grooves orientation does not influence the NiTi wire cyclic fatigue. Material and methods: Segments of NiTi wire (Moreli, Sorocaba, Brazil) measuring 30mm and with a 0.40mm of diameter were used. Grooves were created in the longitudinal direction, at 45 degrees and 90 degrees. The wire was analyzed with SEM and the roughness was quantified by interferometry. The number of cycles until fracture (NCF) was determined by the cyclic fatigue test. Results: the roughness between 45 and 90 degrees groups presented differences (p<0.05). The group without grooves presented the highest NCF (p<0.05). The group with 45 degrees grooves presented better NCF in comparison to the group with 90 degrees (p<0.05). Conclusions: the direction of the grooves influences the fatigue life. The NCF increases with the reduction of the angle of the grooves in relation to the long axis, regardless of the depth of the grooves (AU).

Effects of clinical use of NiTi reciprocating instruments on cyclic and torsional resistance, and on roughness

Abstrac The aim of the present study was to evaluate the cyclic fatigue, torsional resistance and surface roughness of Reciproc R25 instruments in four different situations, namely as new instruments and as instruments tested after clinical preparation of one, two or three maxillary molars with four root canals. The total time required to perform each root canal preparation was recorded. Cyclic fatigue resistance was determined by the time to fracture using a customized testing device (n = 10 per group). The torsional test evaluated the torque and angle of rotation to failure according to ISO 3630-1 (n = 10 per group). The roughness of the working parts of new and used instruments was evaluated with a profilometer (n = 5 per group). Statistical analysis was performed using one-way ANOVA and Tukey's test. The level of significance was set at 5%. No fractures or deformations were observed after clinical use. Higher preparation time was needed during the third use of the instruments for all root canals (p < 0.05). There were no significant differences among the groups in regard to either cyclic fatigue or torsional resistance (p > 0.05). Regarding the roughness measurements, groove depth was higher on new and one- versus two- or three-maxillary-molar-prepared instruments (p < 0.05). It can be concluded that the clinical use of Reciproc instruments increased preparation time and decreased surface roughness. However, clinical use did not affect the cyclic fatigue or torsional resistance of the Reciproc instruments.

Correlação dos diâmetros e conicidades de instrumentos reciprocantes com cones de guta-percha para obturação com cone único / Correlation of the diameters and tapers of reciprocating instruments with gutta-percha points for single-cone root canal filling

Objetivo: o presente estudo teve como objetivo caracterizar as dimensões dos instrumentos Reciproc R25 e X1 Blue File, e dos cones de guta-percha da Mk Life R25, Reciproc R25 e DiaDent R25, para verificar qual cone de guta-percha se adapta melhor no preparo dos instrumentos. Métodos: dez instrumentos Reciproc R25 25/0,08v e X1Blue File 25/0,06; e dez cones de guta-percha Dia- Dent R25, Mk Life R25 e Reciproc R25 foram utilizados. As imagens foram obtidas através de uma lupa estereoscópica com uma câmera digital acoplada. As medidas foram obtidas através do programa TS View. Os diâmetros dos instrumentos e dos cones de guta-percha foram determinados em D0 até D9, com intervalos de medidas de 1,0 mm; e a conicidade foi calculada adotando-se os diâmetros D8 e D1. Os resultados obtidos foram submetidos à análise estatística utilizando o programa Primer of biostatistics versão 6.0. Resultados: apesar da maior conicidade dos instrumentos X1Blue file (0,07mm/mm), não houve diferença estatisticamente significativa entre os instrumentos nos três primeiros milímetros (p > 0,05), o mesmo ocorreu para a conicidade dos cones (p > 0,05). Os cones de guta-percha apresentaram diferença estatisticamente significativa em todos os diâmetros aferidos (p < 0,05). Conclusão: os instrumentos e os cones de guta-percha atenderam à recomendação das respectivas normas ANSI/ADA. O cone de guta-percha que apresentou maior compatibilidade dimensional com os diâmetros dos instrumentos foi o MK life, e VDW foi o que apresentou maior desajuste (AU).

Objective: The aim of this study was to characterize the dimensions of the Reciproc R25 and X1 Blue File instruments and the gutta-percha points of Mk Life R25, Reciproc R25 and DiaDent R25 to verify which gutta-percha point better fits to the instruments preparation. Material and methods: Ten Reciproc R25 25/0.08v and X1Blue File 25/0.06 instruments; and ten DiaDent R25, Mk Life R25 and Reciproc R25 gutta-percha points were used. The images were obtained through a stereomicroscopic with a digital camera coupled. The measurements were obtained through the TS View program. The diameters of instruments and gutta-percha points were determined in D0 through D9 at 1.0 mm intervals, and the taper was calculated by adopting diameters D8 and D1. The results were submitted to statistical analysis using the program Primer of biostatistics version 6.0. Results: Despite the greater taper of the X1Blue file instruments (0.07mm /mm), there was no statistically significant difference between the instruments in the first 3 millimeters (p> 0.05), the same was observed for the tapers of the guta-percha points (p> 0.05). The gutta-percha points presented a statistically significant difference in all measured diameters (p <0.05). Conclusion: Gutta-percha points and instruments have met the recommendations of their respective ANSI/ADA standards. The gutta-percha point that presented greater dimensional compatibility with the diameters of the instruments was the MK life, and VDW presented the greatest mismatch (AU).

Fadiga cíclica e resistência torcional de instrumentos reciprocantes tratados termicamente tipo Gold / Cyclic fatigue and torsional resistance of Gold-type thermally treated reciprocating instruments

Objetivo: o objetivo do presente estudo foi avaliar a fadiga cíclica e torcional dos instrumentos WA1 e WaveOne Gold. Métodos: vinte instrumentos do sistema WA1 (25/0,07v) e vinte instrumentos do sistema WaveOne Gold (25/0,07v) foram utilizados. A resistência à fadiga cíclica foi testada, medindo o tempo até a fratura em um canal artificial curvo de aço inoxidável com ângulo de 80° e raio de curvatura de 3 mm (n = 10). O torque máximo e ângulo de rotação no momento da falha dos instrumentos (n = 10) foram medidos de acordo com a norma ISO 3630-1. A superfície de fratura de todos os fragmentos foi examinada com um microscópio eletrônico de varredura. Os resultados foram analisados estatisticamente usando o teste t de Student com um nível de significância de 5%. Resultados: não foram observadas diferenças na vida em fadiga cíclica dos instrumentos testados (p > 0,05). A força máxima de torção dos instrumentos WA1 foi menor do que os instrumentos WaveOne Gold (p < 0,05); entretanto, não foram observadas diferenças no ângulo máximo de rotação de ambos os sistemas (p > 0,05). A fotomicrografia eletrônica de varredura da superfície da fratura revelou características similares e típicas de fadiga cíclica e de falha por torção para os dois tipos de instrumentos. Conclusão: dentro dos resultados do presente estudo, pode-se concluir que os instrumentos WaveOne Gold e WA1 tiveram comportamento similar com relação à fadiga cíclica. No entanto, o instrumento WaveOne Gold apresentou maior deflexão angular à fratura por torção, em comparação aos instrumentos WA1 (AU).

Introduction: The aim of the present study was to evaluate the cyclic and torsional fatigue resistance of WA1 and WaveOne Gold instruments. Methods: Twenty instruments of the WA1 system (25/0.07v) and twenty instruments of the WaveOne Gold system (25/0.07v) were used. The cyclic fatigue resistance was tested by measuring the time to fracture in a stainless steel curved artificial canal with an angle of 80° and a radius of curvature of 3 mm (n = 10). The maximum torque and rotation angle at instrument failure (n = 10) were measured according to ISO 3630-1. The fracture surface of all the fragments was examined with a scanning electron microscope. The results were statistically analyzed using the student t-test with a significance level of 5%. Results: There were no differences in cyclic fatigue life of the tested instruments (P> 0.05). The maximum torsional force of the WA1 instruments was lower than the WaveOne Gold instruments (P <0.05); however, no differences were observed in the maximum rotation angle of both systems (P> 0.05). The scanning electron photomicrographs of the fracture surface revealed similar and typical characteristics of cyclic fatigue and torsional failure for the 2 types of instruments. Conclusion: Within the results of the present study, it can be concluded that WaveOne Gold and WA1 instruments had similar behavior regarding cyclic fatigue. However, WaveOne Gold instruments presented greater angular deflection to torsional fracture than WA1 instruments.

Fatigue resistance of endodontic instruments manufactured in NiTi CM Wire and in conventional NiTi alloy with eletrochemical treatment / Resistência à fadiga de instrumentos endodônticos fabricados em NiTi CM Wire e em niti convencional com tratamento eletroquìmico

ABSTRACT Objective: This study compared the fatigue behavior of endodontic instruments manufactured with conventional NiTi alloy electropolishing, RaCe (FKG Dentaire, LaChauxdeFonds, Switzerland), with instruments manufactured with NiTi CM ​​Wire subjected to thermomechanical treatment, in the manufacturing process, HyFlex CM (Coltène Whaledent, Cuyahoga Falls, Ohio, USA), both with similar geometry and dimensions in order to determine the influence of the manufacturing process in the fatigue resistance. Methods: The methodoly consisted of twenty HyFlex CM and RaCe instruments with D0 0.25 mm, taper 0.06 mm / mm, 25 mm length, both with triangular cross section. The fracture resistance was evaluated by static fatigue test, using a stainless artificial canal with 5mm of radius (86°), recording the time and calculating the number of cycles until fracture occurs (NCF). For statistical analysis the Student t test was used The fractured instruments surface was analyzed by SEM. Results: The NCF was significantly higher for HyFlex CM instruments in comparison with RaCe files (P˂0.05) being 1336% more resistant to fatigue. The analysis of the fractured surface by SEM showed ductile-kind morphological characteristics for both instruments and the absence of plastic deformation. Conclusion: HyFlex CM instruments present higher values ​​of NCF. Thus, it can be concluded that the thermal treatment to which these instruments with CM Wire alloy are submitted makes them more resistant to fracture than Race instruments manufactured with conventional NiTi alloy electropolishing.

RESUMO Objetivo: Este estudo comparou a vida em fadiga de instrumentos endodônticos fabricados com a liga de NiTi convencional com eletropolimento de superfície, RaCe (FKG Dentaire, LaChauxdeFonds, Suiça), com instrumentos fabricados com a liga de NiTi CM Wire, submetidos a tratamento termomecânico, no processo de fabricação, HyFlex CM (Coltene Whaledent, Cuyahoga Falls, Ohio, EUA), ambos com geometria e dimensões semelhantes, visando determinar a influência do processo de fabricação das ligas e do acabamento superficial na resistência à fadiga. Métodos: Foram utilizados vinte instrumentos HyFlex CM e RaCe com D0 0,25mm, conicidade 0,06mm/mm, 25mm de comprimento, ambos com seção transversal triangular. A resistência à fratura foi avaliada através de teste estático de fadiga ciclica, utilizando um canal artificial em aço-inoxidável com 5mm de raio (86°), sendo registrado o tempo e calculado o número de ciclos para ocorrer a fratura (NCF). Para análise estatística empregou-se o teste t de Student. As superfícies de fratura dos instrumentos foram analisadas em MEV. Resultados: O NCF foi significativamente maior para os instrumentos HyFlex CM em comparação com as limas RaCe (p˂0,05), sendo 1336% mais resistentes à fadiga. A análise das superfícies fraturadas em MEV revelou características morfológicas do tipo dúctil para ambos os instrumentos e ausência de deformação plástica. Conclusão: Os instrumentos HyFlex CM apresentaram valores mais elevados de NCF. Deste modo, pode-se concluir que o tratamento térmico a qual estes instrumentos com a liga CM Wire foram submetidos os torna mais resistentes à fratura do que os instrumentos Race, fabricados com a liga de NiTi convencional com eletropolimento.

Influência da conicidade e do ponto de imobilização na flexibilidade dos instrumentos de níquel-titânio rotatórios RaCe / Influence of taper and immobilization point on the flexibility of RaCe nickel-titanium rotary instruments

Objetivo: esse estudo comparou a flexibilidade de instrumentos de níquel-titânio rotatórios com diferentes conicidades, em diferentes diâmetros da haste helicoidal cônica (D3 e D6). Métodos: trinta instrumentos RaCe (FKG, La Chaux-de Fonds, Suíça), #40 (D0 = 40), com 25 mm de comprimento, foram divididos em três grupos (n = 10), de acordo com sua conicidade. No teste de flexão em cantiléver (45 graus), foram realizadas duas avaliações, com cargas aplicadas, em D3 e D6, para cada grupo. Resultados: a comparação das cargas aplicadas em D3 e D6 nos instrumentos RaCe com diferentes conicidades mostrou valores de carga máxima significativamente diferentes para flexionar os instrumentos: D3 < D6, com a flexibilidade em D3 maior do que em D6. A comparação das cargas aplicadas em D3 nos três grupos revelou diferenças significativas entre os grupos (p < 0,0001), enquanto o teste Student-Newman-Keuls (SNK) mostrou diferenças de flexibilidade entre os três grupos: 0,06 < 0,04 < 0,02mm/mm. O mesmo resultado foi encontrado na comparação da força aplicada em D6. Conclusões: a flexibilidade do instrumento aumenta com a redução da conicidade (p < 0,05) e diminui com o aumento no diâmetro do eixo helicoidal (p < 0,05).

Correlação do diâmetro do preparo de uma nova geração de instrumentos de NiTi com as dimensões de cones de guta-percha de sua antiga geração através de uma análise morfométrica / Correlation of the diameter preparation of a new generation of NiTi instrument with the dimensions of gutta-percha points of its old generation through a morphometric analysis

Objetivo: O presente trabalho teve o objetivo de determinar as dimensões e verificar se os instrumentos X1, X2 e X3 atendem as recomendações da norma ANSI/ ADA nº 101 e se os cones de guta-percha F1, F2 e F3 atendem a norma ANSI/ADA nº 78. Material e Métodos: Os resultados dos instrumentos foram comparados com as dimensões dos cones de guta-percha. Foram utilizados 10 instrumentos e 10 cones de cada tipo. As imagens para análise micromorfométrica foram obtidas com uma lupa Opticam e as medidas determinadas com o software TSView versão 7.2.1.7. Os diâmetros em D3, D6 e D9 reais foram comparados com os nominais pelo teste t-student. Os diâmetros dos instrumentos em D3, D6 e D9 foram comparados com os dos cones pelo teste Anova e complementados com teste de comparações múltiplas SNK. Todos os testes adotaram nível de significância α=5%. Resultados: Os resultados obtidos mostraram que há diferença estatisticamente significante entre as dimensões reais e nominais dos instrumentos (p < 0,05). O instrumento X3 apresentou diferença estatisticamente significante em relação ao cone F1 (p < 0,05), onde os valores do cone são menores do que os dos instrumentos. Conclusão: Dentro das limitações deste estudo pôde-se concluir que: os instrumentos X1 e os cones de guta-percha não atenderam as recomendações de suas normas. O cone F1 pode ser uma opção para obturação dos canais modelados com o instrumento X3, porém a termoplastificação se faz necessária.

Objective: The aim of the present study was to verify if the Protaper Next instruments X1, X2, and X3 and the Protaper Universal gutta-percha cones F1, F2, and F3 meet the ANSI/ADA 101 and 78 recommendations. Material and Methods: The instruments' dimensions were compared with those obtained by the gutta-percha cones. For this, ten instruments and ten cones of each type were used. Micromorphometric images were obtained and analyzed through a stereomicroscope (OptiCam) and measurements were obtained with TSView software, version 7.2.1.7. The D3, D6, and D9 diameters were compared with the nominal diameters using the Student's t-test. After this, the real diameters of the instruments D3, D6, and D9 were compared with the gutta-percha cone diameters by Anova supplemented with SNK test for multiple comparisons. A p ≤0.05 was considered significant. Results: The results showed statistically significant differences between the real diameter and nominal diameter of the instruments (p <0.05). The X3 instrument showed a statistically significant difference when compared to the F1 cone (p <0.05), and the cone values were lower than the instrument values. Conclusion: Within the limitations of this study, it can be concluded that: 1) the X1 instrument and the gutta-percha points did not meet the recommendations, and 2) the F1 cone can be an option for filling the modeled channels with the X3 instrument, but termoplastification is required.

Revisão de literatura das propriedades físico-químicas e biológicas de um cimento à base de silicato de cálcio / Literature review of physicochemical and biological properties of a calcium silicate base

Objetivo: O objetivo do presente trabalho foi revisar as publicações prévias sobre o EndoSequence BC Sealer com o intuito de avaliar os resultados obtidos por este cimento em relação às suas propriedades biológicas e físico-químicas, analisando-se, assim, de forma mais consistente, diversos âmbitos de sua atuação e possíveis desfechos de seu uso clínico realizar uma revisão de literatura sobre este material. Material e Métodos: Uma busca extensiva na literatura foi realizada para identificação de todos os artigos publicados sobre o cimento EndoSequence BC Sealer, considerando-se estudos que avaliaram suas propriedades biológicas e físico-químicas. A estratégia de busca foi fundamentada no acesso às bases de dados PubMed e Bireme. Resultados: Trinta e dois artigos satisfizeram os critérios de inclusão e foram utilizados na presente revisão. Os artigos demonstraram que o cimento possui radiopacidade, escoamento, solubilidade e alteração dimensional adequadas. Além disso, o cimento possui atividade antimicrobiana e é biocompatível. Conclusão: A avaliação dos trabalhos prévios do EndoSequence BC Sealer permite concluir que o cimento EndoSequence BC Sealer demonstrou performance satisfatória quanto as propriedades necessárias para um material obturador endodôntico.

Objective: The aim of this study was to review the previous publications of the EndoSequence BC Sealer in order to evaluate the results obtained using this sealer with regards to its biological and physicochemical properties; therefore, analyzing several areas of its performance and possible outcomes of its clinical use in a more reliable way. Material and Methods: A search of the literature was performed for the identification of all published articles using the EndoSequence BC Sealer, considering studies that evaluated its biological and physicochemical properties. The strategy of the search was based on access to the PubMed and Bireme databases. Results: Thirty-two manuscripts met the inclusion criteria and were used in this review. These manuscripts demonstrated that the sealer has adequate radiopacity, flow, solubility, and dimensional changes. Furthermore, the sealer has antimicrobial activity and is biocompatible. Conclusion: A review of the relevant literature suggests that the EndoSequence BC Sealer has demonstrated satisfactory performance in some important properties for a root canal sealer

Avaliação das propriedades físico-químicas e mecânicas de instrumentos endodônticos de NiTi convencional e com memória controlada / Evaluation of physicochemical and mechanical properties of NiTi endodontic instruments made with conventional and controlled-memory alloys

Objetivo: avaliar a composição semiquantitativa, a exibilidade e a microdureza de instrumentos endodônticos de ligas com NiTi convencional e com memória controlada (CM). E também avaliar a in uência da rotação contínua e do movimento reciprocante na resistência dos instrumentos submetidos à fadiga cíclica. Métodos: os instrumentos Hy ex CM 40/0.04 e RaCe 40/0.04 foram submetidos aos testes de exibilidade, EDS e microdureza. A fadiga cíclica estática foi avaliada em rotação contínua, 150° horá- rio/30° anti-horário; 75° horário/15° anti-horário. Resultados: o Hy ex CM é mais exível que o RaCe (p < 0,05), mas não houve diferença signi cativa quanto à microdureza (p>0,05). O RaCe tem 55,7%wt Ni e 44,3%wt Ti, enquanto o Hy ex CM tem 50,81%wt Ni e 42,28%wt Ti. O movimento reciprocante aumentou signi cativamente a resistência à fadiga cíclica dos instrumentos avaliados, quando comparado à rotação contínua (p < 0,05). O Hy ex CM foi signi cativamente mais resistente no movimento reciprocante de menor ângulo, quando comparado com o de maior ângulo (p<0,05), enquanto não houve diferença para o RaCe (p > 0,05). O Hy ex CM apresentou maior resistência à fadiga do que o RaCe, em todos os movimentos avaliados (p < 0,05). Conclusão: o Hy ex CM tem maior exibilidade e menor percentual de Ni quando comparado ao RaCe, mas ambas apresentaram microdureza similar. O Hy ex CM teve resistência à fadiga cíclica maior do que o RaCe, em todos os movimentos. Os dois instrumentos tiveram maior resistência à fadiga no movimento reciprocante do que na rotação contínua. A menor angulação do movimento reciprocante promoveu maior resistência à fadiga, quando comparada com a de maior amplitude.

Influência de diferentes métodos de fabricação no comportamento mecânico de instrumentos endodônticos de níquel-titânio / Influence of different manufacturing methods on the mechanical behavior of nickel-titanium endodontic instruments

Objetivo: Avaliar o comportamento mecânico de instrumentos endodônticos de NiTi K3 (Sybron Endo,Orange, CA), fabricados convencionalmente e K3XF(Sybron Endo, Orange, CA), submetidos a tratamento térmico na fabricaçÆo.Métodos: Foram utilizados 20 instrumentos K3 e K3XF com D0 0,25 mm, conicidade 0,06 mm/mm e 25 mm de comprimento. Para estandardizaçÆo, dez instrumentos de cada tipo foram examinados sob estereomicroscópio e dois instrumentos (K3 e K3XF) tiveram suas secçães transversais analisadas em microscópio eletrônico de varredura (MEV). A flexibilidade e resistência à fratura foram avaliadas em ensaio de flexÆo em 45° e em teste estático de fadiga, respectivamente. Dez instrumentos K3 e K3XF foram utilizados em cada teste, registrando-se os valores da carga flexural e o número de ciclos para ocorrer a fratura (NCF). Para análise estatística empregou-se o teste t de Student. Os instrumentos fraturados foram analisados em MEV. Resultados: A carga flexural foi significativamente maior para as limas K3 do que para as K3XF (p˂0,05), apresentando, respectivamente, os valores de 713,5 g e 536,4 g. O NCF foi significativamente maior para os instrumentos K3XF em comparaçÆo com as limas K3 (p˂0,05). A análise das superfícies fraturadas em MEV revelou características morfológicas do tipo dúctil para ambos os instrumentos e ausência de deformaçÆo plástica. ConclusÆo: Os instrumentos de NiTi submetidos a tratamento térmico apresentaram os menores valores de força para serem flexionados em 45° e os mais elevado valores de NCF. Desse modo, pode-se inferir que os instrumentos submetidos ao tratamento térmico diferenciado (K3XF) sÆo mais flexíveis e mais resistentes à fratura por fadiga do que os instrumentos K3, fabricados convencionalmente...

Objective: To evaluate the mechanical behavior of K3 NiTi endodontic instruments (Sybron Endo, Orange, CA, USA) with conventional manufacturing or subjected to a thermal treatment during manufacturing (K3XF instruments; Sybron Endo). Methods: Twenty K3 and K3XF instruments with D0 0.25 mm, 0.06 mm/mm taper and 25 mm length were used. For standardizing purposes, 10 instruments of each type were examined by a stereomicroscope and two instruments (K3 and K3FX) had their cross-sections analyzed by scanning electron microscopy (SEM). Flexibility and fracture strength were evaluated by 45° bending test and static fatigue test, respectively. Ten K3 and K3FX instruments were used for each test, obtaining the flexural load values and the number of cycles to failure (NCF). Student?s t test was used for statistical analysis. The fractured instruments were examined by SEM. Results: The flexural load was significantly greater for the K3 than for the K3FX (p<0.05) instruments, 713.3 g and 536.4 g, respectively. The NCF was significantly greater for the K3FX than for the K3 instruments (p<0.05). SEM analysis of the fractured surfaces revealed ductile-type morphological characteristics for both types of instruments and absence of plastic deformity.Conclusion: NiTi instruments subjected to thermal treatment presented lower flexural strength values when subjected to 45º bending and greater NCF values. It may be assumed that the instruments subjected to a special thermal treatment during the manufacturing process (K3FX) are more flexible and more resistant to fatigue fracture than the conventional K3 instruments...

Influência dos comprimentos dos arcos de um canal na fratura por fadiga de instrumentos de níquel-titânio mecanizados

Objetivo: o objetivo desse estudo foi avaliar a influência do comprimento do arco de um canal artificial no número de ciclos necessários para induzir a fratura por fadiga de um instrumento endodôntico de níquel-titânio(NiTi) mecanizado. Métodos: os instrumentos usados nesse trabalho foram os Mtwo de diâmetro em D0 de0,35mm, de conicidade 0,02mm/mm e comprimento de 25mm. Os instrumentos foram utilizados em dois canais artificiais metálicos com segmentos curvos, sob velocidade de 300rpm. As curvaturas estavam localizadas nas extremidades dos canais e possuíam diferentes comprimentos de arcos. O dispositivo usado para o teste de flexão rotativa dos instrumentos endodônticos selecionados foi o descrito previamente por Lopes et al. Resultados: o número de ciclos necessários para causar a fratura por fadiga foi influenciado pelo comprimento do arco do canal artificial. Conclusão: o número de ciclos necessários para induzir a fratura por fadiga nos instrumentos usados em flexão rotativa em canais artificiais de mesmo comprimento de raio diminuiu com o aumento do comprimento do arco

Fratura dos instrumentos endodônticos. Recomendações clínicas / Fracture of endodontic instruments. Clinical recommendations

Instrumentos endodônticos são ferramentas metálicas, fabricados de ligas de aço inoxidável oude niquel-titânio (NiTi) empregados como agentes mecânicos na instrumentação de canais radiculares. Durante a instrumentação do canal radicular, o instrumento sofre tensões que variam com a anatomiado canal. Tensões, desconhecimento das propriedades mecânicas dos materiais e pouca habilidade e experiência clínica do profissional podem induzir sua ruptura no interior do canal. A fratura durante o uso clínico pode ocorrer por carregamento de torção, flexão rotativa e por suas combinações. Instrumentos fraturados e retidos no interior do canal podem afetar o resultado do tratamento endodôntico. O propósito deste trabalho é apresentar recomendações clínicas para reduzir o risco de fraturas de instrumentos endodônticos durante a instrumentação de canais radiculares.

Um instrumento NiTi fabricado por torção: morfologia e propriedades mecânicas / A NiTi rotary instrument manufactured by twisting: morphology and mechanical properties

A morfologia da superfície dos instrumentos TF® foi estudada utilizando estereomicroscopia e microscopia eletrônica de varredura (MEV). Ensaios mecânicos foram feitos para aferir a flexibilidade e a microdureza. Quatro conicidades de instrumentos TF® foram utilizadas (0,04;0,06; 0,08 e 0,10mm/mm). A estereomicroscopia associada com o programa AxioVision® foi utilizada para medir o ângulo da ponta, a conicidade e o diâmetro da ponta dos instrumentos. A MEV foi utilizada para identificar defeitos na superfície provenientes da fabricação e do acabamento.A flexibilidade e a microdureza foram aferidas com os ensaios de flexão e microdureza Vickers, respectivamente.A análise mostrou que o fabricante atendeu aos valores recomendados pela norma nº 28 ANSI/ADA. Os resultados da microscopia eletrônica de varredura mostraram muitos defeitos de superfície e distorção da aresta lateral dos instrumentos.Foi observado que a flexibilidade do instrumento muda com a conicidade. As forças para induzir a transformação de fase por tensão nos instrumentos com conicidade 0,04; 0,06 e 0,08mm/mm foram de 100gf, 150gf e 250gf,respectivamente. Os valores da microdureza Vickers dos instrumentos são compatíveis com os encontrados nos instrumentos fabricados pelo processo de usinagem.

Objectives: The surface morphology of TF® endodonticinstruments was studied using stereomicroscopy and scanningelectron microscopy (SEM). Mechanical tests weredone for flexibility and microhardness. Methods: Fourtapers of TF® files were used (0.04; 0.06; 0.08 and 0.10mm/mm). The stereomicroscopy associated with the AxioVision® program was used to measure the tip angle, thehelical angle, the taper and the tip diameter of the instruments.SEM was used to identify surface defects due to machiningand finishing. The flexibility and the microhardnesswere measured with bending and microhardness Vickerstests, respectively. Results and Conclusion: The analysisshowed that the manufacturer complied with the valuesrecommended by the ANSI/ADA standard number 28. TheSEM results showed many surface defects and a distortionof the instrument helix. It was observed that the instrumentflexibility changes with its taper. The forces to induce thephase transformation by stress on instruments with taper0.04; 0.06 and 0.08 mm/mm were 100 gf, 150 gf and 250gf, respectively. The values of Vickers microhardness of theinstruments are compatible with rotary instruments manufacturedby the machining process.